Mastermix Mortar Mix is our general purpose brick and block laying mortar. It is suitable for general use in the building and construction industry as an original construction and repair product.
We batch produce our premix mortar mix to ensure consistency and incorporate a plasticiser to maximise the workability of the product.
Mortar Mix is suitable for general use in the building and construction industry:
Independent laboratory tests have shown that Mortar Mix has a compression of 41.0MPa after 7 days and 55.0MPa after 28 days. Mortar Mix meets NZ Standard 4210:1989 Code of Practice for masonry construction.
If you are looking for a high strength premix Mortar Mix suitable for brick and block laying than our Super Mortar Mix bag was custom developed and manufactured for you.
You can expect the same level of batch created consistency as our general use Mortar Mix. Only taken a step further with a compression strength of 69.5MPa after 28 days compared to the 55MPa compression strength delivered by our standard Mortar Mix!
Super Mortar Mix is most suitable for projects where high compression strength is required:
Independent laboratory tests have shown that Super Mortar Mix has a compression of 53.0MPa after 4 days, and 69.5MPa after 28 days.
We developed a waterproof mortar mix designed to line areas where water is to be stored, from water tanks, reservoirs and water treatment plants. Further, it will provide, a breathable, waterproof rendered finish to the external walls of houses and commercial buildings.
Typically, waterproof mortar mix products compromise compression strength in order to maximise waterproofing capabilities however our premix waterproof mortar delivers an above standard 27MPa after 28 days.
Waterproof Mortar Mix is most suitable for projects which come into contact with water:
Independent Independent laboratory tests have shown that that Waterproof Mortar Mix has a compressive strength of 22.5 MPa after 7 days and 27.0 MPa after 28 days. It meets NZ Standards 4210:1989 Code of Practice for masonry construction.
We developed our premix Fire Mortar Mix bags to withstand temperatures of between 1500 to 1800ºC making it suitable for most high temperature applications.
In addition it has the additional feature of having a very high compression strength combined with extremely low rate of shrinkage. Fire Mortar Mix forms an extremely heat resistant barrier which builds strength fast:
Fire Mortar Mix is most suitable for projects which come into contact with high temperature:
Independent laboratory tests have shown that that Fire Mortar Mix has a compressive strength of 53.0MPa after 3 days and minimum 70.0MPa after 28 days. It meets NZ Standards 4210:1989 Code of Practice for masonry construction.